Grain refinement in low SFE and particle-containing nickel aluminium bronze during severe plastic deformation at elevated temperatures

Abstract

The influence of particle size and morphology on grain refinement in low stacking fault energy (SFE) alloys was studied by comparing the grain structures in single- and multi-phase Al-bronze (AB) alloys following equal channel angular pressing (ECAP) between 350 and 500 °C. In particular, nickel aluminium bronze (NAB) was chosen as it contained both coarse and fine rounded particles, as well as a lamellar phase which evolved during ECAP. Grain refinement in the single-phase alloy was achieved through dynamic recrystallisation initiated at deformed twin boundaries. By contrast, different mechanisms were observed in the particle-containing NAB. Recrystallisation around the coarse κII particles..